THE EFFECT OF CERAMIC WASTE AS COARSE AGGREGATE ON STRENGTH PROPERTIES OF CONCRETE
DOI:
https://doi.org/10.4314/njt.363.1378Keywords:
Ceramic Waste, Aggregate, Compressive strength, Splitting Tensile Strength, Cost AnalysisAbstract
This paper reports the findings on an experimental investigation of the effect of partial replacement of coarse aggregate with ceramic waste on strength properties of concrete. Compressive strength tests were conducted using 150x150x150mm cube specimens, while tensile strength was investigated using 150x300mm cylinder specimens. Results of tests show that workability, density, compressive and flexural strength of concrete decreased with increase in ceramic waste content. The compressive strength at 90 days curing age for the control sample was 24.67 N/mm2. Compressive strength values at 90 days curing age for 25%, 50% and 75% replacement levels were 21.78 N/mm2, 19.85 N/mm2and 17.85 N/mm2 respectively. The decrease in density and strength was due to ceramic waste being lighter and more porous than normal coarse aggregate. Tensile strength of concrete with ceramic waste decline gradually from 8.39 N/mm2 to 6.13 N/mm2 for the control and 75% replacement samples respectively. This could be attributed to the water absorption capacity and external porcelain nature of the waste material. A production cost savings of 10.7% for 1:2:4 concrete mix was noted at 75% replacement level. This study concludes that ceramic waste could be used for both structural and non-structural works and recommends that beyond 75% replacement level, ceramic waste material should not be used in concrete structures where strength is the major consideration.
Downloads
Published
Issue
Section
License
The contents of the articles are the sole opinion of the author(s) and not of NIJOTECH.
NIJOTECH allows open access for distribution of the published articles in any media so long as whole (not part) of articles are distributed.
A copyright and statement of originality documents will need to be filled out clearly and signed prior to publication of an accepted article. The Copyright form can be downloaded from http://nijotech.com/downloads/COPYRIGHT%20FORM.pdf while the Statement of Originality is in http://nijotech.com/downloads/Statement%20of%20Originality.pdf
For articles that were developed from funded research, a clear acknowledgement of such support should be mentioned in the article with relevant references. Authors are expected to provide complete information on the sponsorship and intellectual property rights of the article together with all exceptions.
It is forbidden to publish the same research report in more than one journal.